ZM-41 Smooth machine cement-lime plaster

Plaster

Universal fine grain plaster, manufactured industrially in the form of a dry mixture using mineral binding fillers and modifying agents, improving the operational properties. After mixing with water forms a uniform plaster solution, easy in processing, with high adhesion to the substrate. Suitable for interior and exterior works.

Use ZM-41 of the plaster solution

The solution is designed for machine or manual application of smooth multi-layer plaster coatings directly on the walls with ceramic elements on lime-sand and concrete substrates. Allowed to use as a base coat for decorative plaster and paint.

Technical data:

  • Composition: dry hydrated lime, Portland cement, mineral fillers, modifying additives
  • Bulk density of fresh solution: about 1,60 g/cm3
  • Bulk density of hardened solution: about 1,40 g/cm3
  • Compressive strength after 28 days: category CSII
  • Flexural strength after 28 days: ≥ 1,0 MPa
  • Adhesion to the substrate and the degree of cracking: ≥ 0,2 MPa; FP: W
  • Air content: about 18%
  • Water absorption caused by capillary suction: category W0
  • Vapour permeability coefficient μ: 7,3
  • Heat conductivity coefficient λ(table value): < 0,67 W /(m*K)
  • Reaction to fire: class A1
  • Size of filler: up to 0,5 mm
  • Soluble chromium content VI: ≤ 0,0002%
  • Package: 25 kg bags
  • Storage: up to 6 months from the manufacturing date in a dry place in original sealed packages
Operating temperature plaster solution

Operating temperature: from +5oC to +25oC

Mixing proportions

Mixing proportions: about 6 l of water per 25 kg of dry mixture

Suitability time plaster solution

Suitability time: about 3 hours (at the temperature of +20oC and air humidity of about 60%) after mixing with water; about 1 hour at the ambient temperature of higher than +25oC after mixing with water

Thickness of layer: 5-15mm

Consumption plaster solution ZM-41

Consumption: about 1,25 kg/m2 per 1 mm of the thickness of the solution layer